301 Stainless Steel Coil

It is mainly a narrow and long steel plate produced to meet the needs of industrial production of famous gold houses or mechanical products in different industrial sectors.

Tel:+86 18018372311

Email:[email protected]


Product Description

The 301 stainless steel belt is a kind of metastable austenitic stainless steel with complete austenitic structure under the condition of sufficient solution.

In stainless steel, 301 is the most easily cold deformation strengthening steel grade, through the cold deformation processing can make the strength of steel, hardness, and retain enough plastic and toughness, together with the steel under the condition of the atmosphere with good rust resistance, but the poor corrosion resistance, reducing medium in acid and alkali salt chemical medium corrosion resistance is poorer, therefore is not recommended for corrosion harsh environment.

The 301 is mainly used in cold working condition for equipment parts that bear high loads and want to reduce the weight of the equipment and do not rust.

In addition, this steel is easy to produce work hardening when impacted by external forces and can absorb more impact energy, which will provide a more reliable safety guarantee for equipment and personnel.

The 301 is prone to work hardening during deformation and is used in places requiring higher strength


Width1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
LengthSince the custom
Surface2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc
FinishHot rolled coil (HR), Cold rolled coil (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form Coils, Foils, Rolls, Plain coil, Shim coil, Perforated coil, Chequered coil, Strip, Flats,
Blank (Circle), Ring (Flange) etc.


12Cr17Ni7 ≤0.15≤2.0≤1.00≤0.045≤0.0316.0~18.0/6.0-8.0-

Yield strength (N/mm2) ≥205

Tensile strength ≥520 Elongation (%) ≥40

Hardness HB ≤187 HRB≤90 HV ≤200

The density of 7.93 g · cm – 3

Specific heat c (20 ℃) 0.502 j. (g · c) – 1

Thermal conductivity λ/W(m·℃)-1 (at the following temperatures /℃)20 100 500 12.1 16.3 21.4

Linear expansion coefficient α/(10-6/℃) (at the following temperatures /℃) 20 ~ 100 20 ~ 200 20 ~ 300 20 ~ 400 16.0 16.8 17.5 18.1

Resistivity 0.73 Ω·mm2·m-1

Melting point 1398 ~ 1420℃

Mechanical properties of

Tensile strength σb (MPa) : ≥520

Conditional yield strength σ0.2 (MPa) : ≥205

Elongation Δ5 (%) : ≥40

Section shrinkage ψ(%) : ≥60

Hardness: 187 hb or less;

90 HRB or less;

200 hv or less

Heat treatment specification and metallographic structure

Heat treatment specification: solution 1010 ~ 1150℃ quick cooling.

Metallographic structure: The structure is characterized by austenitic type.